PEEK tube, whose Chinese name is polyetheretherketone pipe, PEEK tube not only has better heat resistance than other high temperature resistant plastics, but also has high strength, high modulus, high fracture toughness and excellent dimensional stability. PEEK tubes made of high-performance PEEK materials are widely used in various industries, especially in oil and gas industry and semiconductor industry. PEEK is often the first choice for materials due to the comprehensive requirements of service temperature, chemical resistance, creep resistance, thermal stability and compression resistance.
Nanjing Yuwei has been focusing on PEEK production and processing for many years, and has the ability to produce PEEK pipes and PEEK rings of different sizes. We produce PEEK tubes and PEEK rings by extrusion molding, compression molding, injection molding and mechanical molding. We can customize the sizes of PEEK tubes and PEEK rings according to the customer's requirements.
16 years of experience in production and R & D of PEEK, PI, PPS and other profiles and parts.
Advanced and mature PEEK profile extrusion production line.
Have the ability of injection molding and machining PEEK parts of various specifications.
Continuous extrusion production line, large injection molding machine, molding machine, five axis machining center, high precision CNC lathe and other processing equipment.
3D coordinate projector, friction and wear testing machine, microcomputer controlled electronic universal testing ma chine, surface hardness tester, etc.
Extruding PEEK rod, sheet, tube and other profiles with com prehensive specifications and large stock.
All kinds of PEEK filaments and capillaries are extruded.
PEEK profile extrusion can be customized according to cus tomer requirements.
Tick comprehensively analyze the material properties and constantly improve the formulation design and process.
Strictly control the enterprise standards and quality inspection process to ensure the factory quality of each product.
It has a good cooperative relationship with the raw material suppliers such as Victrex, vespl, German engineering plastics and other raw materials suppliers in the UK, with stable raw materials sources.
| Test items | Test criteria | Test conditions | Units | NJSSPEEK-1000 | NJSSPEEK-G1030 | NJSSPEEK-C1030 |
|---|---|---|---|---|---|---|
| Pure resin | 30% glass fiber | 30% carbon fiber | ||||
| Density | ISO1183 | Crystal | g/cm3 | 1.3 | 1.51 | 1.4 |
| Water absorption rate (3.2mm thick tensile bar, soaking test) | ISO62-1 | 24h, 23℃ | % | 0.07 | 0.04 | 0.05 |
| Balance, 23℃ | % | 0.4 | 0.4 | 0.3 | ||
| Tensile strength | ISO527 | Yield, 23℃ | MPa | 100 | 175 | 122 |
| Elongation at break | ISO527 | Fracture, 23℃ | % | 20 | 2.7 | 2.5 |
| Bending strength | ISO178 | Yield, 23℃ | MPa | 165 | 265 | 268 |
| Bending modulus | ISO178 | 23℃ | GPa | 4.1 | 11.3 | 8.9 |
| Compressive strength | ISO604 | 23℃ | MPa | 125 | 250 | 193 |
| Impact strength of simply supported beam | ISO179/1eA | There is a gap | kJ/m2 | 7 | 8 | 7 |
| ISO179/1U | No gap | kJ/m2 | 55 | 38 | ||
| Impact strength of cantilever beam | ISO180/A | There is a gap | kJ/m2 | 7.5 | 10 | 9 |
| ISO180/U | No gap | kJ/m2 | - | 60 | 45 | |
| Shore D hardness | ISO868 | 23℃ | 85 | 88 | 88 | |
| Melting point | ISO11357 | - | ℃ | 343 | 343 | 343 |
| Glass transition temperature | ISO11357 | Start | ℃ | 143 | 143 | 143 |
| Specific heat capacity | DSC | 23℃ | kJ/kg℃ | 2.2 | 1.7 | 1.8 |
| Coefficient of thermalexpansion | ISO11359 | Below Tg along the flow direction | ppm/K | 45 | 18 | 5 |
| Below Tg along the flow direction | ppm/K | 120 | 18 | 6 | ||
| Heat distortion temperature | ISO75-f | 1.8Mpa | ℃ | 152 | 315 | 315 |
| Thermal conductivity | ISO22007-4 | 23℃ | W/mK | 0.29 | 0.3 | 0.95 |
| Dielectric strength | IEC60243-1 | 2mm | kV/mm | 23 | 25 | - |
| Dielectric constant | IEC60250 | 23℃,1KHz | - | 3.1 | 3.2-3.4 | - |
| 23℃,50Hz | - | 3 | - | - | ||
| Volume resistivity | IEC60093 | 23℃,1V | Ω·cm | 1016 | 1016 | 105 |
| 275℃ | Ω·cm | 109 | - | - |
| OD(mm) | ID(mm) | length(mm) | Weight(kg) |
|---|---|---|---|
| 30 | 10 | 1000 | 0.94 |
| 30 | 15 | 1000 | 0.82 |
| 30 | 20 | 1000 | 0.68 |
| 40 | 25 | 1000 | 1.23 |
| 45 | 25 | 1000 | 1.69 |
| 50 | 30 | 1000 | 1.93 |
| 70 | 40 | 1000 | 3.83 |
| 70 | 50 | 1000 | 3.15 |
| Other specifications can be customized | |||
Focus on the R&D, design, production and composite modification of special engineering plastics such as PEEK, PI, PPS and PEI.
Have the ability of continuous extrusion molding, injection molding, compression molding, machining molding and other molding processes.
Design, processing, manufacturing and modification of extrusion mold, compression mold and injection mold.
PEEK, PI, PPS, PEI and other parts and products are customized according to drawings and samples.